Non-combustible, high-temperature resistant, abrasion-resistant insulating panel for heat and flame protection, as thermal insulation, sealing sheet and composite material in mechanical and plant engineering. When thermally loaded, free of smoke and toxic gases. Dust-free (dust-bound), hygienically harmless.
- excellent insulation value of 0.03 W/mK at 200 °C (average temperature)
- usable up to 800 °C without shrinkage
- weight per unit area: 1.7 kg/m² ± 10%
- temperature resistance: up to 600 °C flexible up to 800 °C dimensionally stable solidified
- ignition loss: 24 h 600 °C ≤ 3.5% 24 h 800 °C ≤ 4.0%
- shrinkage:
- after 24 hrs at 600 °C area 0% thickness 0%
- after 24 h at 800 °C area 0% thickness 0%
- after 24 h at 1000 °C area 4.7% thickness 0%
- thermal conductivity: 0.030 W/mK at average temperature 200 °C
- density: approx. 1 g/cm³
- water absorption: 50% of dry weight
- after 14 days of underwater storage:
- no shrinkage or swelling in area and thickness
- material property unchanged. Fire behaviour: non-combustible according to DIN 4102 – class A
- after 14 days of underwater storage:
- fire behaviour: non-combustible according to DIN 4102 – class A1
Sheet thickness: 2.2 mm ± 0.5 mm
Available in sheets of 1,000 x 1,000 mm , 1,500 x 1,000 mm or 2,000 x 1,000 mm
or as water-jet cuttings or stamped parts according to drawings.
Dimension | Thickness |
1.000 x 1.000 mm |
2,2 mm ± 0,5 mm
|
1.500 x 1.000 mm | |
2.000 x 1.000 mm |
Building material classification according to DIN 4102: A1 – non-combustible
It can be processed with scissors, punch or saw.
Heat protection, flame protection, thermal insulation, sealing plate and composite material, e.g. in thermal plants.
-
USEABLE UP TO800 °CWITHOUT SHRINKING
-
INSULATING VALUE OF0,03 W/mKat 200 °C